API 5L Line Pipe
- BEILAI
- CHINA
API 5L LINE PIPE
OD:21.3mm-610mm
Wall Thickness:2.77mm-59.54mm
Line pipe mainly used for transportation of gas, water oil. Sour service pipeline is intended for solving the problem of cracking and leakage caused by insufficient resistance to sulfide stress corrosion cracking and hydrogen induced cracking under acidic service environment when developing in acid oil and gas exploration.
Standards and technical terms of products
API SPEC 5L Specification for line pipe
ISO 3183 Petroleum and natural gas industries-steel pipe for pipeline transportation system.
GB/T9711 Pipe line used for transport system in oil and gas industry
ASME B36.10 Welded and seamless wrought steel pipe
ANSI/NACE MR0175 Metals for sulfide stress cracking and stress corrosion cracking resistance in sour oilfield
ANSI/NACE TM0177 Laboratory testing of metal for resistance to sulfide stress cracking and stress Corrosion cracking in H2S environment
ISO15156 Petroleum and natural gas industries -materials for use in H2S containing environment in oil and gas production
Size
OD:21.3mm-610mm
Wall Thickness:2.77mm-59.54mm
DN(mm) | NPS(in) | OD(mm) | 10 | 20 | 30 | STD/40 | 60 | XS/80 | 100 | 120 | 140 | 160 | XXS |
15 | 1/2 | 21.3 | 2.77 | 3.73 | 4.78 | 7.47 | |||||||
20 | 3/4 | 26.7 | 2.87 | 3.91 | 5.56 | 7.82 | |||||||
25 | 1 | 33.4 | 3.38 | 4.55 | 6.35 | 9.09 | |||||||
32 | 1 1/4 | 42.2 | 3.58 | 4.85 | 6.35 | 9.70 | |||||||
40 | 1 1/2 | 48.3 | 3.68 | 5.08 | 7.14 | 1.015 | |||||||
50 | 2 | 60.3 | 3.91 | 5.54 | 8.74 | 11.07 | |||||||
65 | 2 1/2 | 73.0 | 5.16 | 7.01 | 9.53 | 14.02 | |||||||
80 | 3 | 88.9 | 5.49 | 7.62 | 11.13 | 15.24 | |||||||
90 | 3 1/2 | 101.6 | 5.74 | 8.08 | |||||||||
100 | 4 | 114.3 | 6.02 | 8.56 | 11.13 | 13.49 | 17.12 | ||||||
125 | 5 | 141.3 | 6.55 | 9.53 | 12.70 | 15.88 | 19.05 | ||||||
150 | 6 | 168.3 | 7.11 | 10.97 | 14.27 | 18.26 | 21.95 | ||||||
200 | 8 | 219.1 | 6.35 | 7.04 | 8.18 | 10.31 | 12.70 | 15.08 | 18.26 | 20.62 | 23.01 | 22.23 |
Chemical composition
Grade | Chemical composition/% Max | |||||||
C | Si | Mn | P | S | V | Nb | Ti | |
L245/B | 0.28 | - | 1.20 | 0.030 | 0.030 | - | - | - |
L290/X42 | 0.28 | - | 1.30 | 0.030 | 0.030 | - | - | - |
L320/X46 | 0.28 | - | 1.40 | 0.030 | 0.030 | - | - | - |
L360/X52 | 0.28 | - | 1.40 | 0.030 | 0.030 | - | - | - |
L390/X56 | 0.28 | - | 1.40 | 0.030 | 0.030 | - | - | - |
L415/X60 | 0.28 | - | 1.40 | 0.030 | 0.030 | - | - | - |
L450/X65 | 0.28 | - | 1.40 | 0.030 | 0.030 | - | - | - |
L485/X70 | 0.28 | - | 1.40 | 0.030 | 0.030 | - | - | - |
Note: Date in the composition of PSL1:PSL2 The composition can be negotiated by both parties | ||||||||
Mechanical property requirements
Grade | Yield strength/Mpa | Yield strength/Mpa | Yield ratio | CVN/J | ||||||
PSL1(Min) | PSL2 | PSL1(Min) | PSL2 | PSL1(Min) | PSL2 | |||||
-N,Q | -NS,QS | -N,Q | -NS,QS | -N,Q | -NS,QS | |||||
L245/B | 245 | 245~450 | 245~450 | 415 | 415~655 | 415~655 | - | ≤0.93 | ≤0.93 | ≥27 |
L290/X42 | 2900 | 290~495 | 290~495 | 415 | 415~655 | 415~655 | - | |||
L320/X46 | 320 | 320~525 | 320~525 | 435 | 435~655 | 435~655 | - | |||
L360/X52 | 360 | 360~530 | 360~530 | 460 | 460~760 | 460~760 | - | |||
L390/X56 | 390 | 390~545 | 390~545 | 490 | 490~760 | 490~760 | - | |||
L415/X60 | 415 | 415~565 | 415~565 | 520 | 520~760 | 520~760 | - | |||
L450/X65 | 450 | 450~600 | 450~600 | 535 | 535~760 | 535~760 | - | |||
L485/X70 | 485 | 485~635 | 485~635 | 570 | 570~760 | 570~760 | - | |||
L555/X80 | 555~705 | 625~825 | ≥40 | |||||||
Note:Line pipe for other special service environment will be manufactured based on the negotiation resule of both sides. | ||||||||||